Quantum confined intense red luminescence from large area monolithic arrays of mesoporous and nanocrystal-decorated silicon nanowires for luminescent devices
O'Dwyer, Colm; McSweeney, William; Collins, Gillian
We report intense red luminescence from mesoporous n+-Si(100) nanowires (NWs) and nanocrystal-decorated p-Si NWs fabricated using electroless metal assisted chemical (MAC) etching. n+-Si NWs are composed of a labyrinthine network of silicon nanocrystals in a random mesoporous structure. p-type Si(100) NWs exhibit solid core structure, with a surface roughness that contains surface-bound nanocrystals. Both mesoporous n+-Si NWs and rough, solid p-Si NWs exhibit red luminescence at ∼1.7 and ∼1.8 eV, respectively. Time-resolved photoluminescence (PL) measurements indicated long (tens of μs) radiative recombination lifetimes. The red luminescence is visible with the naked eye and the red light is most intense from mesoporous n+-Si NWs, which exhibit a red-shift in the emission maximum to 1.76 eV at 100 K. The red PL from monolithic arrays of p-type NWs with nanocrystal-decorated rough surfaces is comparatively weak, but originates from the surface bound nanocrystals. Significant PL intensity increase is found during excitation for mesoporous NWs. X-ray photoelectron spectroscopy identifies a stoichiometric SiO2 on the rough p-Si NWs with a SiOx species at the NW surface. No distinct oxide is found on the mesoporous NWs. The analysis confirms that long life-time PL emission arises from quantum confinement from internal nanoscale crystallites, and oxidized surface-bound crystallites, on n+- and p-Si NWs respectively.
Keyword(s): Etching; Microscopy; Nanocrystal; Nanomaterials; Nanowires; Photoluminscence; Porous; Silicon
Publication Date:
2015
Type: Journal article
Peer-Reviewed: Yes
Language(s): English
Institution: University College Cork
Funder(s): Higher Education Authority; Science Foundation Ireland
Citation(s): O'Dwyer, C., McSweeney, W. and Collins, G. (2016) 'Quantum Confined Intense Red Luminescence from Large Area Monolithic Arrays of Mesoporous and Nanocrystal-Decorated Silicon Nanowires for Luminescent Devices', ECS Journal of Solid State Science and Technology, 5(1), pp. R3059-R3066. doi: 10.1149/2.0081601jss
Publisher(s): Electrochemical Society
File Format(s): application/pdf
Related Link(s): http://jss.ecsdl.org/content/5/1/R3059.abstract?cpetoc
First Indexed: 2018-05-10 06:30:17 Last Updated: 2018-05-10 06:30:17