Electrochemical properties of Cu deposition from methanesulphonate electrolytes for ULSI and MEMS applications
Hasan, Maksudul; Casey, Declan P.; Rohan, James F.
Methanesulphonic acid (MSA) is an alternative to sulphuric acid electrolytes. The electrochemical nucleation and growth of Cu on a glassy carbon (GC) electrode was studied from the methanesulphonate and sulphate baths. The overpotential for Cu deposition was much smaller in the MSA bath compared to the traditional sulphuric acid bath. Cu nucleation occurred at a higher rate in the MSA bath. The measured diffusion coefficient value for Cu deposition from the MSA bath was 6.82 x 10-6 cm2/s. The UV-Vis spectroscopic results confirmed that the coordination of Cu species was the same in both electrolytes. Cu electrodeposition on Ni sputtered Si substrate from the high efficiency MSA bath was found to be photoresist compatible with no void formation. 1D Cu nanorods were also deposited through AAO template on a Ni evaporated seed layer substrate showing potential applications as interconnects in ULSI and MEMS.
Keyword(s): Electrochemical properties; Electrolytes; Glassy carbon; Nanorods; Nucleation; Photoresists; Sulfuric acid; AAO template; Cu deposition; Cu species; Diffusion; Coefficients; Electrochemical nucleation; Glassy carbon electrodes; High efficiency; MEMS applications; Methanesulphonate; Methanesulphonic acid; Overpotential; Potential applications
Publication Date:
2009
Type: Journal article
Peer-Reviewed: Yes
Language(s): English
Institution: University College Cork
Funder(s): Enterprise Ireland
Citation(s): Hasan, M., Casey, D. and Rohan, J. (2009) 'Electrochemical Properties of Cu Deposition from Methanesulphonate Electrolytes for ULSI and MEMS Applications', ECS Transactions, 19(24), pp. 57-66. doi: 10.1149/1.3246598
Publisher(s): Electrochemical Society
File Format(s): application/pdf
Related Link(s): http://ecst.ecsdl.org/content/19/24/57
First Indexed: 2019-03-12 06:31:45 Last Updated: 2019-03-12 06:31:45